用羧基化碳纳米管修饰玻碳电极制备了一种新型的碳纳米管修饰电极(A).利用循环伏安,交流阻抗法对A进行了表征.用线性扫描伏安(LSV)法研究了A对Vc的电催化行为,结果表明,在0.1 mol.L-1的醋酸缓冲液(pH5.8)中,当Vc在A表面于-1.0 V电位下富集30 s,电位扫速为100 mV.s-1时,Vc在LSV图上能出现一灵敏的电催化氧化峰,峰电位约为0.149 V;利用该氧化峰可以进行痕量Vc的测定;峰电流与Vc浓度在1.0×10-5mol.L-1~1.0×10-3mol.L-1内成良好线关系,其相关系数为0.996,检出限达1.0×10-6mol.L-1;A稳定性较好,可用于水果和蔬菜中Vc的现场快速检测,回收率96.0%~103.0%

A novel carboxylic carbon nanotubes modified electrode（A） was prepared by carboxylic multi-walled carbon nanotubes modified glass carbon electrode.A was characterized by cyclic voltammetry and alternating current impedance.The electrocatalytic property of A on Vc was investigated by linear sweep voltammetry.The experimental results showed that there was a sensitive oxidation peak on voltammogram and the peak potential was about 0.149 V when accumulation time of Vc at A surface was 30 s at-1.0 V and potential scan rate was 100 mV·s^-1 in 0.1 ...